Polyester based powder coating MT-JA220G White

OEM	OEM Services Provided
Feature	Easy to Use Eco-friendly
Classification	Powder Coating
Advantage	Professional, Fast Delivery, Customizable
Samples	Apply for free，Contact us now. ↓↓↓

Email WhatsApp

Product Description

MT-JA220G is a polyester based powder coating, formulated using TGIC and is designed for exterior exposure offering excellent light and weather resistance from a single coat finish.

Powder Properties

Chemical type	Polyester TGIC
Appearance	Smooth Matt
Particle Size	Suitable for electrostatic spray
Specific gravity	1.60 ± 0.05 g/cm³
Film Thickness	75 – 100 microns
Coverage	8.3 m2/kg @ 75 microns
Storage	Dry cool conditions below 25°C (open boxes must be resealed)
Shelf life	12 months
Stoving schedule (object temperature)	10 minutes @ 200°C

Test Conditions

The results shown below are based on mechanical and chemical tests which (unless otherwise indicated) have been carried out under laboratory conditions and are given for guidance only. Actual product performance will depend upon the circumstances under which the product is used.

Substrate	Cold Rolled Steel
Pretreatment	Degreased panels (mechanical tests) Zn/Mn phosphate steel (chemical tests)
Film Thickness	60 - 80 microns
Stoving Schedule	10 minutes at 200°C

Mechanical Tests

	test	results
Flexibility	ASTM D522	5mm
Adhesion	ASTM D3359	100%
Impact (direct	ASTM D2794	50kgcm
Erichsen Cupping	ISO 1520	>5mm
Gloss(@60°）	ISO 2813	25 ± 5
Hardness (scratch)	ASTM D3363	H
Reflectance Class	DIN EN 16268	B

Pre-treatment

Steel surfaces to be coated must be clean and free from grease, mill scale and rust. For maximum protection, it is essential to pre-treat components prior to the application of MT-JA220G. Iron phosphate and zinc phosphate pre-treatment of ferrous substrates improve corrosion resistance. Aluminium substrates may require a chromate conversion coating.

Application

MT-JA220G can be applied using manual or automatic electrostatic spray equipment. It is recommended, that for consistent application and appearance, the product be fluidized during application. Unused powder can be reclaimed using suitable equipment and recycled through the coating system.

Consult Now